PERBAIKAN KEKERASAN DAN STRUKTUR MIKRO LOGAM KUNINGAN SEBAGAI BAHAN PROPELLER DENGAN METODE SHOT PEENING

Margono Margono, Yanti Pasmawati, Nugroho Tri Atmoko, Rizqi Ilmal Yaqin, Bambang Hari Priyambodo

Abstract


Brass metal is widely used as a supporting equipment material, one of which is a propeller. The propeller itself is one component of the boat that rotates and produces thrust energy. The continuous use of propellers results in degradation or a decrease in quality and service life. The degradation of the propeller is affected by the hardness, toughness, and corrosion resistance of the working environment. To improve the quality of the propeller, shot peening treatment was carried out on its surface. Shot peening is a continuous shooting process with fine particles in the form of steel balls on the surface of the object. Shot peening can increase the density of the microstructure and produce compressive residual stress which causes the surface hardness to also increase. Shot peening is carried out with variations in duration of 2, 4, 6, 8, and 10 minutes, 100 mm shooting range, and 7 Bar firing pressure. The steel ball particles used have a hardness of 40-50 HRC and a diameter of 5 mm. The results of the hardness test showed an increase in the surface hardness of the spesimens for a duration of 2, 4, 6, 8, and 10 minutes, respectively 189, 294, 302, 324, 330, dan 341 HV. The microstructure of the spesimen after shot peening looks tighter and denser. The highest hardness value is 341 HV or an increase of 80% compared to raw material.

Full Text:

PDF

References


ASTM, & E92. (2017). Standard Test Methods for Vickers Hardness and Knoop Hardness of Metallic Materials. I, 1–27. https://doi.org/10.1520/E0092-17.2

Azis, Muh. A., Iskandar, B. H., & Novita, Y. (2017). Kajian Desain Kapal Purse Seine Tradisional Di Kabupaten Pinrang (Study Kasus Km. Cahaya Arafah). ALBACORE, I(1), 69–76.

Bag, A., Delbergue, D., Ajaja, J., Bocher, P., Lévesque, M., & Brochu, M. (2020). Effect of different shot peening conditions on the fatigue life of 300 M steel submitted to high-stress amplitudes. International Journal of Fatigue, 130. https://doi.org/10.1016/j.ijfatigue.2019.105274

B. H. Priyambodo, Suhartoyo, & Slamet, S. (2020). Increased Corrosion Resistance on Cu35%Zn Surface by Shot Peening Process. Journal of Physics: Conference Series, 1430(1). https://doi.org/10.1088/1742-6596/1430/1/012055

Heydari Astaraee, A., Bagherifard, S., Bradanini, A., Duó, P., Henze, S., Taylor, B., & Guagliano, M. (2020). Application of shot peening to case-hardened steel gears: the effect of gradient material properties and component geometry. Surface and Coatings Technology, 398, 126084. https://doi.org/10.1016/j.surfcoat.2020.126084

Iswanto, P. T., Yaqin, R. I., Akhyar, & Sadida, H. M. (2020). Influence of shot peening on surface properties and corrosion resistance of implant material AISI 316L. Metalurgija, 59(3), 309–312.

Kondo, Y., Siahaya, Y., & Leonard, J. (2012). Analisis Investasi Pada Industri Pengecoran Propeller Kapal (Studi Kasus : Cv. Antero Jaya Sakti). Jurnal Mekanikal, 3(1), 231–239.

Lasabuda, R. (2013). Pembangunan Wilayah Pesisir Dan Lautan Dalam Perspektif Negara Kepulauan Republik Indonesia. Jurnal Ilmiah Platax, I(2), 92–101.

Liu, L., & Chi, R. (2019). Effect of microstructure on high cycle fatigue behavior of brass processed by laser shock peening. Materials Science and Engineering A, 740–741, 342–352. https://doi.org/10.1016/j.msea.2018.10.108

Llaneza, V., & Belzunce, F. J. (2015). Study of the effects produced by shot peening on the surface of quenched and tempered steels: Roughness, residual stresses and work hardening. Applied Surface Science, 356, 475–485. https://doi.org/10.1016/j.apsusc.2015.08.110

Majzoobi, G. H., & Abbasi, F. (2017). On the effect of shot-peening on fretting fatigue of Al7075-T6 under cyclic normal contact loading. Surface and Coatings Technology, 328, 292–303. https://doi.org/10.1016/j.surfcoat.2017.08.067

Maleki, E., Unal, O., Reza Kashyzadeh, K., Bagherifard, S., & Guagliano, M. (2021). A systematic study on the effects of shot peening on a mild carbon steel: Microstructure, mechanical properties, and axial fatigue strength of smooth and notched specimens. Applied Surface Science Advances, 4(October 2020), 100071. https://doi.org/10.1016/j.apsadv.2021.100071

Margono, Priyambodo, B. H., & Yaqin, R. I. (2021). Shot Peening on AISI 304 by Various Sizes of Steel Ball Particles to Reduce Corrosion Rates. The Journal of Corrosion Science and Engineering, 23, 1–8

M. Benedetti, V. Fontanari, B. Winiarski, P.J. Withers, M. Allahkarami, and J. C. H. (2015). Fatigue Behavior of Shot Peened Notched Specimens: Effect of the Residual Stress Field Ahead of the Notch Root. Procedia Engineering, 109, 80–88. https://doi.org/10.1016/j.proeng.2015.06.210

Priyambodo, B. H., Margono, & Nugroho, K. C. (2022). Corrosion Protection on AISI 304 by Shot Peening Treatment with Variation of Particle Size and Shooting Pressure. Materials Science Forum, 1051, 153–159. https://doi.org/10.4028/www.scientific.net/msf.1051.153

Priyambodo, B. H., Margono, Nugroho, K. C., Atmoko, N. T., & Yaqin, R. I. (2022). Effect of Oil Quenching and Shot Peening to Improve Hardness Behavior of S45C Carbon Steel. Materials Science Forum, 1067, 27–33. https://doi.org/10.4028/p-dt2v5c

Priyambodo, B. H., Slamet, S., Suhartoyo, & Sriyanto. (2018). Peningkatan Ketahanan Korosi Pada Permukaan Cu40zn Dengan Proses Shot Peening Variasi Tekanan Tembak. Prosiding SNATIF Ke -5, 655–660

Priyambodo, B. H., Suhartoyo, & Slamet, S. (2017). Studi Pengaruh Shot Peening Pada Permukaan Cu35Zn Terhadap Ketahanan. Prosiding SNATIF Ke-4 Tahun 2017, 153–160

Priyambodo, B. H., Yaqin, R. I., Margono, & Nugroho, K. C. (2021). Pengaruh Perlakuan Annealing Dan Shoot Peening Terhadap Kekerasan Dan Struktur Mikro Pada Baja Karbon JIS S45C. JTT (Jurnal Teknologi Terapan), 7(2), 138–144

Sakamoto, J., Lee, Y. S., & Cheong, S. K. (2015). Effect of surface flaw on fatigue strength of shot-peened medium-carbon steel. Engineering Fracture Mechanics, 133, 99–111. https://doi.org/10.1016/j.engfracmech.2014.11.005

Salam, H. A. H., Mulyatno, I. P., & Iqbal, M. (2017). Analisa Kelelahan Propeller Kapal Ikan PVC Dengan Metode Elemen Hingga. Jurnal Teknik Perkapalan, 5(1), 243–252

Sherafatnia, K., Farrahi, G. H., & Mahmoudi, A. H. (2018). Effect of initial surface treatment on shot peening residual stress field: Analytical approach with experimental verification. International Journal of Mechanical Sciences, 137, 171–181. https://doi.org/10.1016/j.ijmecsci.2018.01.022

Slamet, S., Priyambodo, B. H., Suhartoyo, & Yaqin, R. I. (2018). Pengaruh Durasi Waktu Shot Peening Pada Permukaan Logam Kuningan Terhadap Ketahanan Korosi. Prosiding SNATIF Ke -5, 661–666

Taufikurrahman, Safei, & Hardianto, I. (2005). Analisa Sifat Mekanik Bahan Paduan Tembaga-Seng Sebagai Alternatif Pengganti Bantalan Gelinding pada Lori Pengangkut Buah Sawit. Jurnal Teknik Mesin, 7(2), 77–84

Wang, Y., Xie, H., Zhou, Z., Li, X., Wu, W., & Gong, J. (2020). Effect of shot peening coverage on hydrogen embrittlement of ferrite-pearlite steel. International Journal of Hydrogen Energy, 45(11), 7169–7184




DOI: https://doi.org/10.31884/jtt.v9i2.431

Refbacks

  • There are currently no refbacks.


Copyright (c) 2023 JTT (Jurnal Teknologi Terapan)

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

View Stats

 

 Creative Common Attribution-ShareAlike 4.0 International (CC BY-SA 4.0)